Improvement of Lithium Storage Performance of Silica Anode by Using Ketjen Black as Functional Conductive Agent

In this paper, SiO2 aerogels were prepared by a sol–gel method. Using Ketjen Black (KB), Super P (SP) and Acetylene Black (AB) as a conductive agent, respectively, the effects of the structure and morphology of the three conductive agents on the electrochemical performance of SiO2 gel anode were systematically investigated and compared. The results show that KB provides far better cycling and rate performance than SP and AB for SiO2 anode electrodes, with a reversible specific capacity of 351.4 mA h g−1 at 0.2 A g−1 after 200 cycles and a stable 311.7 mA h g−1 at 1.0 A g−1 after 500 cycles. The enhanced mechanism of the lithium storage performance of SiO2-KB anode was also proposed.


Introduction
Lithium-ion batteries (LIBs) have attracted much attention due to their high energy density and long cycle life. To meet the demand for scaled-up LIBs, the development of electrode materials with high performance is necessary. Graphite is widely used as anode material for LIBs [1], however, its theoretical lithium storage capacity is relatively low, only 372 mA h g −1 . Therefore, silicon-based anode materials with higher theoretical specific capacity (4200 mA h g −1 ) are considered to be anode materials for next-generation LIBs [2][3][4]. However, the severe volume expansion (>300%) associated with the various phase transitions during the intercalation and escape of lithium in/out Si particles have been a major disadvantage, as this led to rapid capacity fading and significantly limited commercial application [5]. Although novel silicon anodes with nanosphere [6,7], nanotube [8,9], core-shell structure [10,11] and other new structures could improve the cycling performance [12,13], the complicated process and expensive preparation technology are prohibitive. In addition, the low initial coulombic efficiency and the poor conductivity also limited its application [14][15][16]. Compared to elemental Si anode, silicon oxides show a smaller volume change during cycling. Furthermore, when using silicon oxides as anodes, the in situ generated Li 2 O and lithium silicates during the first lithiation may buffer the large volume change and lead to the improvement of cycling stability. In cutting-edge researches, silica [17] with hollow [18], porous [19,20], and other special structures were composited with carbon [19,21,22], graphite [23], metal [24], and metal oxides [25][26][27][28] to improve its conductivity and lithium storage performance. These methods could effectively improve the electrochemical performance of silica anodes.
Carbon conductive agents, which were added during the electrode manufacturing process, played an important role in the impedance and electrode density. However, their functional mechanism still needs further investigation [29,30]. The literature has reported that conductive agents could be used as the mediator [31] to form a conductive network in electrodes, reducing the contact resistance of the electrode and improving the electron transport rate. Commercial carbon black, such as acetylene black (AB) and Super-P (SP), have been used as conductive agents in LIBs [32,33]. Compared with AB and SP, Ketjen Black (KB) has the advantages of large specific surface area, excellent electrical conductivity, and relatively narrow pore size distribution, when used as the conductive agent [34]. However, the systematic study of the effect of KB on silica anodes is sparsely reported.
Herein, a network nanostructure of silica (SiO 2 ) anode material using KB as a conductive agent with high electrochemical performance was prepared. The effects of KB on the electrochemical performance of silica anode materials were systematically studied. Furthermore, the enhanced storage mechanism of the SiO 2 -KB anode materials was proposed. This work revealed that the type of conductive agent played a key role on the electrochemical performance of anode materials.

Synthesis
Briefly, SiO 2 aerogels were prepared by the sol-gel method [35]. It was obtained by taking 8 mL of anhydrous ethanol in a beaker, adding ammonia to adjust the pH to 9-10, then slowly adding 0.5 mL of TEOS, and left for 4 h at room temperature before adding 1 mL of deionized water to prepare the gel, and freeze-drying to obtain SiO 2 aerogels.
SiO 2 nanospheres were obtained by first taking 3 mL of NH 3 ·H 2 O and 60 mL of alcohol to be mixed and stirred thoroughly, then 1.5 mL of TEOS was added into the above solution and continued stirring for 10 h at room temperature to obtain a white emulsion, finally the solid product was collected by centrifugation, washed several times with distilled water and alcohol, and dried at 70 • C for 12 h in a vacuum.

Materials Characterization
Morphological and compositional analyses for the as-prepared sample were performed with Transmission Electron Microscope (TEM, JEM-2100F, JEOL Inc., Tokyo, Japan) and field emission scanning electron microscopy (SEM, S-4800, HITACHI Inc., Tokyo, Japan), respectively, the crystallographic structure of the obtained SiO 2 were characterized by X-ray diffraction (XRD, X' Pert PRO, PANalytical Inc., Almelo, The Netherlands), the chemical component of the SiO 2 anode was investigated using an X-ray photoelectron spectroscope (XPS, ESCALAB 250Xi, Thermo Fisher Scientific Inc., Waltham, MA, USA) using Al kα radiation, the electrical resistance and electrical resistivity were tested by four-point probe meter (FPM, RTS-2A, 4 PROBES TECH Inc., China).

Electrochemical Measurements
The working electrodes were fabricated by compressing a mixture of the active materials (SiO 2 nanospheres), a conductive material of KB, AB, or SP, and a binder of polyvinylidene fluoride at the mass ratio of 50:30:20 onto Cu foil current collector (10 µm in thickness), then dried at 110 • C for 12 h. 0.1 mL of 1 M LiPF 6 in EC/DMC/DEC (Ethylene carbonate/Dimethyl carbonate/Diethyl carbonate) with volume ratio of 1:1:1 was used as the electrolyte, electrochemical experiments of half cells were carried out in CR2025 coin-type cells, 0.6 mm thick lithium discs are used as counter electrodes, and Polypropylene diaphragm type Celgard 2500 as battery separator. The cells were assembled in an argon-filled glove box (MIKROUNA, LAB2000, Shanghai, China). The specific capacity was measured by a galvanostatic discharge-charge method in the voltage range between 3.0 V and 0.01 V at a current density of 100 mA g −1 with SiO 2 as the active material mass on a battery test system (Neware, BTS 5 V 10 mA, Shenzhen, China). Cyclic voltammetry was performed using an electrochemical workstation (CV, CHI 690D, CH Instruments Ins, Wuhan, China) between 3 V and 0.01 V (vs. Li/Li + ) at a scan rate of 0.5 mV s −1 . Figure 1a shows the SEM image of the SiO 2 aerogel, and it can be seen that the prepared SiO 2 aerogel particles are uniform in size with sphere in shape. Figure 1b shows that the average size of SiO 2 aerogel particle is about 100 nm. Figure 1c is the XRD pattern of the SiO 2 aerogel, the crystal structure of the prepared silica aerogel only shows a broad diffraction peak at around 23 • , indicating an amorphous structure. Nanomaterials 2022, 12, x FOR PEER REVIEW 3 of 13 V and 0.01 V at a current density of 100 mA g −1 with SiO2 as the active material mass on a battery test system (Neware, BTS 5 V 10 mA, Shenzhen, China). Cyclic voltammetry was performed using an electrochemical workstation (CV, CHI 690D, CH Instruments Ins, China) between 3 V and 0.01 V (vs. Li/Li + ) at a scan rate of 0.5 mV s −1 . Figure 1a shows the SEM image of the SiO2 aerogel, and it can be seen that the prepared SiO2 aerogel particles are uniform in size with sphere in shape. Figure 1b shows that the average size of SiO2 aerogel particle is about 100 nm. Figure 1c is the XRD pattern of the SiO2 aerogel, the crystal structure of the prepared silica aerogel only shows a broad diffraction peak at around 23°, indicating an amorphous structure.  Figure 2 shows the TEM and elemental mapping images of SiO2 aerogel mixed with different conductive agents, respectively. It can be seen that different conductive agents form different structures when combined with silica aerogel. Figure 2a shows that the aerogel mixture with KB (SiO2-KB) has an internet structure with uniformly dispersed nanoparticles, which indicates that a conductive network can be formed to provide a large number of effective conductive pathways and contacts for Li-ions. Furthermore, the elemental distribution shows a cobweb-like carbon chain pathway. For comparison, we also investigated the differences in the composition of the conductive pathways of SiO2-SP and SiO2-AB, respectively, under identical conditions. Figure 2b shows that the SiO2-SP has a branched structure with larger SiO2 particles and more agglomerates than that of SiO2-KB. Figure 2c shows that the SiO2-AB stacks together and has more agglomerate structure than that of SiO2-SP and SiO2-KB. Therefore, it is clear that the SiO2-KB has the best dispersion, indicating it has excellent conductive network channels.  Figure 2 shows the TEM and elemental mapping images of SiO 2 aerogel mixed with different conductive agents, respectively. It can be seen that different conductive agents form different structures when combined with silica aerogel. Figure 2a shows that the aerogel mixture with KB (SiO 2 -KB) has an internet structure with uniformly dispersed nanoparticles, which indicates that a conductive network can be formed to provide a large number of effective conductive pathways and contacts for Li-ions. Furthermore, the elemental distribution shows a cobweb-like carbon chain pathway. For comparison, we also investigated the differences in the composition of the conductive pathways of SiO 2 -SP and SiO 2 -AB, respectively, under identical conditions. Figure 2b shows that the SiO 2 -SP has a branched structure with larger SiO 2 particles and more agglomerates than that of SiO 2 -KB. Figure 2c shows that the SiO 2 -AB stacks together and has more agglomerate structure than that of SiO 2 -SP and SiO 2 -KB. Therefore, it is clear that the SiO 2 -KB has the best dispersion, indicating it has excellent conductive network channels.

Results and Discussion
To further confirm the effects of the three conductive agents on the electrochemical performance of SiO 2 anode, a four-probe electrical resistance test was carried out and the result is shown in Table 1, the type of conductive agents plays an important role on the electrical resistance of SiO 2 anode. KB provides much lower electrical resistance and electrical resistivity than SP and AB for SiO 2 anode, which is helpful to improve the rate performance of electrode. The cycling performance and coulombic efficiency of the SiO 2 anode with different conductive agents are shown in Figure 3a. The first discharge capacity of SiO 2 -KB reaches 378.2 mA h g −1 , the capacity has a slight decrease in the several consequent cycles, and maintains 351.4 mA h g −1 after 200th cycles at 0.2 A g −1 . In comparison to SiO 2 -KB, electrodes of SiO 2 -SP and SiO 2 -AB exhibit a lower reversible capacity of 139.4 mA h g −1 and 118.7 mA h g −1 at the first cycle and after 100th cycles display the capacity of 163.9 mA h g −1 and 137.7 mA h g −1 at 0.2 A g −1 , respectively, which indicates that KB is more beneficial in facilitating the silica electrochemical reaction. The specific capacity of SiO 2 -KB decreased before the first 40 cycles, and then gradually increased, even after more than 100 cycles; the former is mainly due to the gradual lithiation of SiO 2 and the generated irreversible products such as lithium silicate and Li 2 O, and the latter is due to the generated elemental silicon, which can provide the reversible specific capacity by the Si-Li alloy reaction. To further confirm the effects of the three conductive agents on the electrochemical performance of SiO2 anode, a four-probe electrical resistance test was carried out and the result is shown in Table 1, the type of conductive agents plays an important role on the electrical resistance of SiO2 anode. KB provides much lower electrical resistance and electrical resistivity than SP and AB for SiO2 anode, which is helpful to improve the rate performance of electrode. The cycling performance and coulombic efficiency of the SiO2 anode with different conductive agents are shown in Figure 3a. The first discharge capacity of SiO2-KB reaches 378.2 mA h g −1 , the capacity has a slight decrease in the several consequent cycles, and maintains 351.4 mA h g −1 after 200th cycles at 0.2 A g −1 . In comparison to SiO2-KB, electrodes of SiO2-SP and SiO2-AB exhibit a lower reversible capacity of 139.4 mA h g −1 and 118.7 mA h g −1 at the first cycle and after 100th cycles display the capacity of 163.9 mA h g −1 and 137.7 mA h g −1 at 0.2 A g −1 , respectively, which indicates that KB is more beneficial in facilitating the silica electrochemical reaction. The specific capacity of SiO2-KB decreased before the first 40 cycles, and then gradually increased, even after more than 100 cycles; the former is mainly due to the gradual lithiation of SiO2 and the generated irreversible products such as lithium silicate and Li2O, and the latter is due to the generated elemental silicon, which can provide the reversible specific capacity by the Si-Li alloy reaction.   The rate capability of the electrodes is shown in Figure 3b, with different current densities of 0.2, 0.4, 0.6, 0.8, 1.0, 2.0, and 4.0 A g −1 . The SiO 2 -KB electrode attains an average discharge capacity of 318.2 mA h g −1 , 263.6 mA h g −1 , 231.9 mA h g −1 , 213.4 mA h g −1 , 207.7 mA h g −1 , 176.7 mA h g −1 , and 151.4 mA h g −1 , respectively, at the above current densities. The stable high reversible capacity of 331.1 mA h g −1 recovered when the current density turned back to 0.2 A g −1 . Compared to SiO 2 -SP and SiO 2 -AB, SiO 2 -KB shows more excellent rate properties, indicating that the SiO 2 -KB has excellent structural stability.
To determine the origin of the electrochemical behavior of SiO 2 -KB, electrochemical impedance spectra (EIS) test was performed at their open-circuit potential. The equivalent circuits inserted in Figure 3c were employed to analyze the Nyquist plot of the desired anode material. The total impedance could be regarded as the electrolyte resistance R e and the charge transfer resistance R ct , and C dl is the double-layer capacitance. Z w is the Warburg impedance that reflects the diffusion of lithium-ion in the solid. C L means the simplified intercalation capacitance. A semicircle was an indication for the charge transfer at high frequency range, while the straight line for the low frequency lithium-ion diffusion in the electrode material [36]. Obviously, the resistance of SiO 2 -KB (R ct = 130 Ω) is much lower than that of SiO 2 -SP (R ct = 180 Ω) and SiO 2 -AB (R ct = 240 Ω), suggesting that KB could remarkably enhance the silica electrical conductivity. Furthermore, SiO 2 -KB presents an exciting long-term cycling performance and delivers a specific capacity of 311.7 mA h g −1 at a current density of 1.0 A g −1 after 500 cycles. In comparison to SiO 2 -KB, SiO 2 -SP and SiO 2 -AB exhibit a much lower reversible capacity of 66.4 mA h g −1 and 75.9 mA h g −1 , respectively, at the first cycle, and after 500th cycles, the capacity only remains 115.5 mA h g −1 and 123.9 mA h g −1 , respectively, which is shown in Figure 3d.
To confirm the structural integrity of the electrodes after cycle tests, SEM images of the different electrodes with the three conductive agents after 200 cycles were obtained and illustrated in Figure 4. For the electrode of SiO 2 -KB, the shape of SiO 2 remained constant after 200 cycles (Figure 4a,b). For the electrode of SiO 2 -SP, the silica undergoes a slight agglomeration phenomenon after 200 cycles (Figure 4c,d), while for the electrode of SiO 2 -AB, the SiO 2 particles stick together and form large particles after 200 cycles (Figure 4e,f), which reduces the contact area between the silica, and leads to the reduction in capacity.   Figure 5 shows the CV curves of the SiO2 aerogel electrodes at a scan rate of 0.5 mV s −1 with three different conductive agents, respectively. As can be seen in Figure 5, the reduction characteristic peak potential for the reaction of silica to produce lithium silicate and lithium oxide is 0.42 V, 0.65 V, and 0.8 V when using KB, SP, and AB as the conductive agent, respectively. The peak potential is significantly shifted to a smaller voltage for the KB (Figure 5a) compared to the SP (Figure 5b) and AB (Figure 5c). The oxidation characteristic peak potential of 0.25 V for the silicon-lithium alloy when using KB as the conduc-  Figure 5 shows the CV curves of the SiO 2 aerogel electrodes at a scan rate of 0.5 mV s −1 with three different conductive agents, respectively. As can be seen in Figure 5, the reduction characteristic peak potential for the reaction of silica to produce lithium silicate and lithium oxide is 0.42 V, 0.65 V, and 0.8 V when using KB, SP, and AB as the conductive agent, Nanomaterials 2022, 12, 692 6 of 11 respectively. The peak potential is significantly shifted to a smaller voltage for the KB (Figure 5a) compared to the SP (Figure 5b) and AB (Figure 5c). The oxidation characteristic peak potential of 0.25 V for the silicon-lithium alloy when using KB as the conductive agent also shows a significant shift to a smaller voltage compared to the SP (0.28 V) and AB (0.35 V), which is mainly due to the fact that KB has higher conductivity than SP and AB, where KB acts as a microcurrent collector between SiO 2 and the current collector to accelerate the speed of electron movement and also effectively increase the migration rate of Li + in the electrode material. Subsequently, the polarization of the silica anode is reduced, which will facilitate the occurrence of electrochemical reactions [37].  Figure 5 shows the CV curves of the SiO2 aerogel electrodes at a scan rate of 0.5 mV s −1 with three different conductive agents, respectively. As can be seen in Figure 5, the reduction characteristic peak potential for the reaction of silica to produce lithium silicate and lithium oxide is 0.42 V, 0.65 V, and 0.8 V when using KB, SP, and AB as the conductive agent, respectively. The peak potential is significantly shifted to a smaller voltage for the KB (Figure 5a) compared to the SP (Figure 5b) and AB (Figure 5c). The oxidation characteristic peak potential of 0.25 V for the silicon-lithium alloy when using KB as the conductive agent also shows a significant shift to a smaller voltage compared to the SP (0.28 V) and AB (0.35 V), which is mainly due to the fact that KB has higher conductivity than SP and AB, where KB acts as a microcurrent collector between SiO2 and the current collector to accelerate the speed of electron movement and also effectively increase the migration rate of Li + in the electrode material. Subsequently, the polarization of the silica anode is reduced, which will facilitate the occurrence of electrochemical reactions [37].   (Figure 6c) during discharge/charge were identified by XPS, where energy correction for surface contamination was performed using C1s (284.6 eV) as a standard. The Si 2p 3/2 peak shifts from 104.0 to 103.0 eV when discharged to 0.01 V, suggesting the reduction in Si to Li x Si. When charged to 3 V, the peak shifts back to the original position of the SiO 2 electrode before discharge/charge (blue curve). It is clear that the curve in SiO 2 -KB fluctuates more strongly than the smooth curves in SiO 2 -SP and SiO 2 -AB, indicating that the electrochemical reaction promoted by SiO 2 using KB as a conductive agent produces a higher amount of products containing elemental silicon, which is conducive to the improvement of electrochemical performance. LixSi. When charged to 3 V, the peak shifts back to the original position of the SiO2 electrode before discharge/charge (blue curve). It is clear that the curve in SiO2-KB fluctuates more strongly than the smooth curves in SiO2-SP and SiO2-AB, indicating that the electrochemical reaction promoted by SiO2 using KB as a conductive agent produces a higher amount of products containing elemental silicon, which is conducive to the improvement of electrochemical performance. Based on previous researches, the possible electrochemical reaction mechanisms of SiO2 can be summarized into the following reactions [38,39]: Reactions of R1, and R2 are irreversible (potential of KB-0.25 V, SP-0.28 V, AB-0.35 V) and occur simultaneously although they compete with each other, and the obtained Si is electrochemically active, while Li2O, and Li4SiO4 are electrochemically inactive [22]. The reaction R1 can produce more Si and result in a higher capacity than the reaction R2 [13].
To better understand the storage mechanism and excellent high-rate performance of the SiO2 aerogel electrode with KB, the CV curves of the SiO2 aerogel electrode under the three carbon conductive agents at different scan rates from 0.5 to 5 mV s −1 were collected Based on previous researches, the possible electrochemical reaction mechanisms of SiO 2 can be summarized into the following reactions [38,39]: Reactions of R1, and R2 are irreversible (potential of KB-0.25 V, SP-0.28 V, AB-0.35 V) and occur simultaneously although they compete with each other, and the obtained Si is electrochemically active, while Li 2 O, and Li 4 SiO 4 are electrochemically inactive [22]. The reaction R1 can produce more Si and result in a higher capacity than the reaction R2 [13].
To better understand the storage mechanism and excellent high-rate performance of the SiO 2 aerogel electrode with KB, the CV curves of the SiO 2 aerogel electrode under the three carbon conductive agents at different scan rates from 0.5 to 5 mV s −1 were collected and shown in Figure 7a,e,i. Generally, the current obeys a function relationship with the voltage during the sweep [40][41][42][43]: where a and b are the parameters. The capacity contributions from the diffusion-controlled intercalation process and the surface-induced capacitive process can be qualitatively analyzed by the b-value. For a diffusion-controlled process, the b-value is 0.5, while the b-value near 1 means a totally capacitive-controlled process. According to the fitted line log (v)-log (i) curve depicted in Figure 7b,f,j, the b-value is 0.84, 0.86, 0.66, respectively. Furthermore, in view of the capacity contribution, the current (i) under a certain potential (V) can be divided into two parts [42][43][44]: where k 1 v and k 2 v 1 2 present charge stemmed from the surface capacitive charge and diffusion-controlled charge, respectively. The area share of the pseudocapacitive behavior of the silica aerogel electrodes with the three different conductive agents is shown in the paler parts of Figure 7c,g,k. The pseudocapacitance contributions are shown in Figure 7d,h,l. The pseudocapacitance contribution of the SiO 2 aerogel electrode with KB at scan rates of 1.0 to 5.0 mV s −1 is 41%, 49%, 54%, 58% and 61%, respectively; 51%, 58%, 63%, 67% and 70%, respectively, for SP and 65%, 73%, 77%, 79% and 80%, respectively, for AB. It can be seen that the use of different forms of conductive agents has a greater effect on the contribution of the pseudocapacitance in the SiO 2 aerogel electrode. The storage mechanism of the SiO 2 -KB electrode is dominated by diffusion-controlled intercalation behavior, which is due to the excellent conductive network structure of KB and leads to an accelerated redox reaction. The contribution of surface-driven pseudocapacitance behavior for the SiO 2 -KB electrode gradually increases as the scan rate increases, but is still less than that SiO 2 -SP and SiO 2 -AB. The contribution of the pseudocapacitance behavior of the SiO 2 -KB electrode increases with increasing scan rate, however remains smaller than that of the SiO 2 -SP and SiO 2 -AB electrodes.
Li + diffusion coefficients during electrochemical charge/discharge for silica aerogels with different conductive agents calculated from the GITT method [45][46][47] are presented in Figure 8. The voltage change curve of the first charge/discharge under pulse current when using three different carbon conductive agents is shown in Figure 8a, and the Liion diffusion coefficient calculated from the pulse charge/discharge curve is shown in Figure 8b. The longer charging and discharging duration of Li + in the diffusivity test curve of SiO 2 -KB is due to the special network structure of KB, which enables the nano-SiO 2 particles to perform electrochemical reactions without agglomeration and less hindering to the transport of Li + . This indicates that the KB conductive agent accelerates the diffusion of Li + and enables the sufficient electrochemical reaction of SiO 2 [16].
In order to confirm the effect of the KB, the electrochemical properties of SiO 2 nanosphere anode was compared with three different conductive agents, respectively. The morphology of the SiO 2 nanospheres is shown in Figure 9a, which has a nice monodispersity and smooth surface with an average particle size of 100 nm. The inset in Figure 9a shows the XRD pattern of the SiO 2 nanospheres; a broad peak at 23 • suggesting that the SiO 2 nanospheres are amorphous in structure similar to the SiO 2 aerogels. Figure 9b-d show the CV curves of the SiO 2 nanosphere anode at a scan rate of 0.5 mV s −1 when using the three different conductive agents, respectively. The reduction characteristic peak potential for the reaction of SiO 2 to produce Li 2 O and Li 4 SiO 4 locates at 0.5 V for the SiO 2 nanospheres-KB anode, which has a significant shift to the left compared to the anodes of SiO 2 nanospheres-SP (0.85 V) and SiO 2 nanospheres-AB (0.9 V), indicating that it also has the similar effect of reducing polarization of SiO 2 anodes prepared by different methods when using KB as the conducting agent, and strongly promotes the electrochemical reaction.
greater effect on the contribution of the pseudocapacitance in the SiO2 aerogel electrode. The storage mechanism of the SiO2-KB electrode is dominated by diffusion-controlled intercalation behavior, which is due to the excellent conductive network structure of KB and leads to an accelerated redox reaction. The contribution of surface-driven pseudocapacitance behavior for the SiO2-KB electrode gradually increases as the scan rate increases, but is still less than that SiO2-SP and SiO2-AB. The contribution of the pseudocapacitance behavior of the SiO2-KB electrode increases with increasing scan rate, however remains smaller than that of the SiO2-SP and SiO2-AB electrodes. Li + diffusion coefficients during electrochemical charge/discharge for silica aerogels with different conductive agents calculated from the GITT method [45−47] are presented in Figure 8. The voltage change curve of the first charge/discharge under pulse current when using three different carbon conductive agents is shown in Figure 8a, and the Li-ion diffusion coefficient calculated from the pulse charge/discharge curve is shown in Figure 8b. The longer charging and discharging duration of Li + in the diffusivity test curve of SiO2-KB is due to the special network structure of KB, which enables the nano-SiO2 particles to perform electrochemical reactions without agglomeration and less hindering to the transport of Li + . This indicates that the KB conductive agent accelerates the diffusion of Li + and enables the sufficient electrochemical reaction of SiO2 [16]. In order to confirm the effect of the KB, the electrochemical properties of SiO2 nano sphere anode was compared with three different conductive agents, respectively. Th morphology of the SiO2 nanospheres is shown in Figure 9a, which has a nice monodisper sity and smooth surface with an average particle size of 100 nm. The inset in Figure 9a shows the XRD pattern of the SiO2 nanospheres; a broad peak at 23° suggesting that th SiO2 nanospheres are amorphous in structure similar to the SiO2 aerogels. Figure 9b-d show the CV curves of the SiO2 nanosphere anode at a scan rate of 0.5 mV s −1 when using the three different conductive agents, respectively. The reduction characteristic peak po  The function of KB can be described as a schematic diagram conductive network, as shown in Figure 10, the special structure of KB connects the SiO2 aerogel particles together and forms an excellent conductive network of dispersed SiO2-KB, which provides rich electron transfer channels and improves the electrochemical performance of silica anode.

Conclusions
In summary, the effects of the types and the structures of conductive agents on the electrochemical performance of SiO2 aerogel electrode were investigated, and the results show that the KB as a conductive agent not only can uniformly disperse and wrap the SiO2 nanoparticles, but also can build a good conductive network to enhance the transport rate of lithium-ions and effectively increase their electrochemical activity. This work proves and verifies that SiO2 aerogel can be used as a recommended electrode material for high-rate LIBs through choosing appropriate conductive agent.  The function of KB can be described as a schematic diagram conductive network, as shown in Figure 10, the special structure of KB connects the SiO 2 aerogel particles together and forms an excellent conductive network of dispersed SiO 2 -KB, which provides rich electron transfer channels and improves the electrochemical performance of silica anode. The function of KB can be described as a schematic diagram conductive network, as shown in Figure 10, the special structure of KB connects the SiO2 aerogel particles together and forms an excellent conductive network of dispersed SiO2-KB, which provides rich electron transfer channels and improves the electrochemical performance of silica anode.

Conclusions
In summary, the effects of the types and the structures of conductive agents on the electrochemical performance of SiO2 aerogel electrode were investigated, and the results show that the KB as a conductive agent not only can uniformly disperse and wrap the SiO2 nanoparticles, but also can build a good conductive network to enhance the transport rate of lithium-ions and effectively increase their electrochemical activity. This work proves and verifies that SiO2 aerogel can be used as a recommended electrode material for high-rate LIBs through choosing appropriate conductive agent.

Conclusions
In summary, the effects of the types and the structures of conductive agents on the electrochemical performance of SiO 2 aerogel electrode were investigated, and the results show that the KB as a conductive agent not only can uniformly disperse and wrap the SiO 2 nanoparticles, but also can build a good conductive network to enhance the transport rate of lithium-ions and effectively increase their electrochemical activity. This work proves and verifies that SiO 2 aerogel can be used as a recommended electrode material for high-rate LIBs through choosing appropriate conductive agent.